High Flame Retardancy Zirconia Ceramic Part
Application Field
High flame retardancy zirconia ceramic parts have a good prospect. Zirconia ceramic has superior properties such as high strength, high toughness, anti-static, and high temperature resistance, and can be precision machined into various complex shapes with good wear resistance and chemical stability. Therefore, it is widely used in many fields. Especially, high flame retardancy zirconia ceramics have a wide application prospect in the field of fire safety, including fire doors, fire equipment, etc.
With the increase of people's awareness of fire safety and the strengthening of relevant regulations, the demand for zirconia ceramic accessories will continue to increase. , with the continuous improvement of production technology and the continuous reduction of costs, the cost performance of zirconia ceramic accessories will also be continuously improved, further promoting the expansion of their application scope.
In addition, with the continuous development of consumer electronics products towards high-quality and high value-added directions, the application of zirconia ceramic parts in the appearance, fingerprint recognition devices, and lock screen volume keys of consumer electronics products will also be further developed.
In summary, high flame retardancy zirconia ceramic parts have broad application prospects and market demand, and their market size will also continue to expand in the future years.
Details
Quantity requirement: 1pc to 1 million pcs. There is no MQQ limited.
Sample lead time: tooling making is 15days+ sample making 15days.
Production lead time: 15 to 45days.
Payment term: negotiated by both parties.
Production process:
Zirconia(ZrO2) ceramics are also known as an important ceramic material. It is made of zirconia powder through molding, sintering, grinding and machining processes. zirconia ceramics can also be used in various industries, such as shafts. Sealing bearings, cutting elements, molds, auto parts, and even the human body of mechical industry.
Physical & Chemical Data
| Zirconia Ceramic(Zro2) Character Referance Sheet | ||
| Decription | Unit | Grade A95% |
| Density | g/cm3 | 6 |
| Flexural | Mpa | 1300 |
| Compressive strength | Mpa | 3000 |
| Modulus of elasticity | Gpa | 205 |
| Impact resistance | Mpm1/2 | 12 |
| Weibull modulus | M | 25 |
| Vickers hardulus | Hv0.5 | 1150 |
| Thermal Expansion coefficient | 10-6k-1 | 10 |
| Thermal conductivity | W/Mk | 2 |
| Thermal shock Resistance | △T℃ | 280 |
| Max use temperature | ℃ | 1000 |
| Volume resistivity at 20℃ | Ω | ≥1010 |
Packing
Usually use material such as moisture-proof, shock-proof for the products that will be not damaged. We use PP bag and carton wooden pallets according to customer's requirement. Suitable for sea and air transportation.